CSR 8121 Epoxy Lamination Resin

Send Message Add to My Favorites

Description

2-component, colorless, transparent primer. It consists of a hardener mixture and an epoxy resin with special additives. In every set, there are two packages weighed at the factory. It is used to increase the adhesion strength of the system by reducing the suction of the surfaces under the base paint and coatings. It is used in water insulations, for filling cracks in concrete and stones, in carbon fiber lamination


Supplier

Digalpa


Product Category

Adhesives & Sealants

Resins

Epoxy Resins


Last Update

19 August 2015


Appearance

  • Transparent

Application Tools

  • Hard brush
  • Roller

Chemical Resistance?

  • Yes

Colors Available

  • Colorless

Consumption with Roller for 1 Layer [g/m²]

  • 1.000 <--> 1.500

Density of Component A (ASTM D-1475) [g/cm³]

  • 1,13

Density of Component B (ASTM D-1475) [g/cm³]

  • 1,06

Maximum Concrete Application Surface Humidity [%]

  • 5%

Minimum Application Temperature [°C]

  • 5°C

Minimum Pressure Resistance of Concrete Application Surface [kg/cm²]

  • 225

Mixture Density (ASTM D-1475) [g/cm³]

  • 1,1

Mixture Rate A:B (by Weight)

  • 2 : 1

Overpainting Possibility

  • Yes

Pot Life in 10°C [minutes]

  • 300

Pot Life in 20°C [minutes]

  • 30

Pot Life in 30°C [minutes]

  • 25

Pot Life in 40°C [minutes]

  • 20

Recommended for

  • Surfaces under base paints
  • Stones
  • Carbon fiber lamination
  • Surfaces under coatings
  • Waterproofing
  • Concrete
  • Covering active cracks

Shelf Life in Storage Below 25°C (Months)

  • 12

Solvent-Free

  • Yes

Storage Temperature Interval [°C]

  • +5ºC <--> +25ºC

Touchable-Drying Time in 10°C [Hours]

  • 42

Touchable-Drying Time in 20°C [Hours]

  • 20

Touchable-Drying Time in 30°C [Hours]

  • 5

Touchable-Drying Time in 40°C [Hours]

  • 3

Type of Chemical Substance

  • 2-component primer